Railway Industry

    • 6008-T5
      Contact Now

      6008-T5

      Density2.70g/cm3 Density2.71 g/cm3 (169 lb/ft3) Elastic (Young's, Tensile) Modulus70 GPa (10 x 106 psi) Elongation at Break10 to 17 % Specific Heat Capacity890 J/kg-K Strength to Weight Ratio74 to 111 kN-m/kg Tensile Strength: Ultimate (UTS)200 to 300 MPa (29 to 44 x 103...
    • 6005-AT5
      Contact Now

      6005-AT5

      Density2.72g/cm3 Density2.71 g/cm3 (169 lb/ft3) Elastic (Young's, Tensile) Modulus70 GPa (10 x 106 psi) Electrical Conductivity50 % IACS Elongation at Break11 % Melting Onset (Solidus)605 °C (1120 °F) Shear Modulus26 GPa (3.8 106 psi) Specific Heat Capacity890 J/kg-K...
    • 5083-H321
      Contact Now

      5083-H321

      Density2.66 g/cm3 (166 lb/ft3) Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi) Electrical Conductivity29 % IACS Elongation at Break15 % Melting Onset (Solidus)574 °C (1070 °F) Shear Modulus27 GPa (3.9 106 psi) Specific Heat Capacity900 J/kg-K Strength to Weight...
    • 7050-T7452
      Contact Now

      7050-T7452

      Density2.80 g/cm3 (175 lb/ft3) Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi) Elongation at Break8 to 9 % Specific Heat Capacity800 J/kg-K Strength to Weight Ratio193 to 196 kN-m/kg Tensile Strength: Ultimate (UTS)540 to 550 MPa (78 to 80 x 103 psi) Tensile...
    • 7N01
    • 7020-T4
      Contact Now

      7020-T4

      Density2.78 g/cm3 (174 lb/ft3) Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi) Elongation at Break15 % Melting Onset (Solidus)605 °C (1120 °F) Shear Modulus26 GPa (3.8 106 psi) Specific Heat Capacity870 J/kg-K Strength to Weight Ratio129 kN-m/kg Tensile Strength:...
    • 5083-H112
      Contact Now

      5083-H112

      Density2.66 g/cm3 (166 lb/ft3) Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi) Electrical Conductivity29 % IACS Elongation at Break16 % Melting Onset (Solidus)574 °C (1070 °F) Shear Modulus27 GPa (3.9 106 psi) Specific Heat Capacity900 J/kg-K Strength to Weight...
    • 5083-O
      Contact Now

      5083-O

      Density2.66 g/cm3 (166 lb/ft3) Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi) Electrical Conductivity29 % IACS Elongation at Break17 % Fatigue Strength (Endurance Limit)150 MPa (22 x 103 psi) Melting Onset (Solidus)574 °C (1070 °F) Shear Modulus27 GPa (3.9 106...
Asian Aluminium Depot Co.,Ltd is one of the top level China railway industry manufacturers and suppliers with one the most famous bulk brands, if you are going to wholesale customized bulk railway industry in stock or you are looking for high-speed rail material, high-speed rail product, metro mount pad for draft sill, profile for roof connection of subway carriage, high-speed rail profile, carriage body profile free sample, we are always at your services.

Our Service

The company have a good and long-term strategic cooperative relationship with Chinalco, Nanshan Aluminum, WANJI Aluminium, ZhongFu Industrial, and so on which are domestic well-known brand aluminium manufacturers.

Feedback

Contact Us

Address:No.78 Gucheng Road(M.) Yushan Town, Kunshan City, Jiangsu Provice, China

Tel: +0086-512-36630592

Fax: +0086-512-36630595

E-mail: info@al-plate.com

CopyRight© Asian Aluminium Depot Co.,Ltd