Moulding And Tools

    • 7075-T651
      Contact Now

      7075-T651

      Density2.80 g/cm3 (175 lb/ft3) Elastic (Young's, Tensile) Modulus72 GPa (10 x 106 psi) Electrical Conductivity33 % IACS Elongation at Break10 % Melting Onset (Solidus)477 °C (890 °F) Shear Modulus27 GPa (3.9 106 psi) Specific Heat Capacity960 J/kg-K Strength to Weight...
    • 7075-T6
      Contact Now

      7075-T6

      Density2.80 g/cm3 (175 lb/ft3) Elastic (Young's, Tensile) Modulus72 GPa (10 x 106 psi) Electrical Conductivity33 % IACS Elongation at Break10 % Fatigue Strength (Endurance Limit)160 MPa (23 x 103 psi) Melting Onset (Solidus)477 °C (891 °F) Shear Modulus27 GPa (3.9 106...
    • 6061-T651
      Contact Now

      6061-T651

      Density2.70 g/cm3 (169 lb/ft3) Elastic (Young's, Tensile) Modulus69 GPa (10 x 106 psi) Electrical Conductivity43 % IACS Elongation at Break12 % Melting Onset (Solidus)582 °C (1080 °F) Shear Modulus26 GPa (3.8 106 psi) Specific Heat Capacity900 J/kg-K Strength to Weight...
    • 6061-T6
      Contact Now

      6061-T6

      Density2.70 g/cm3 (169 lb/ft3) Elastic (Young's, Tensile) Modulus69 GPa (10.0 x 106 psi) Electrical Conductivity43 % IACS Elongation at Break15 % Fatigue Strength (Endurance Limit)97 MPa (14 x 103 psi) Melting Onset (Solidus)582 °C (1080 °F) Shear Modulus26 GPa (3.8 106...
    • 5052-H112
      Contact Now

      5052-H112

      Density2.68 g/cm3 (167 lb/ft3) Elastic (Young's, Tensile) Modulus70 GPa (10 x 106 psi) Electrical Conductivity35 % IACS Elongation at Break17 % Melting Onset (Solidus)607 °C (1120 °F) Shear Modulus26 GPa (3.8 106 psi) Specific Heat Capacity900 J/kg-K Specific Heat...
    • 7021-Sawn
      Contact Now

      7021-Sawn

      Density2.78 g/cm3 (174 lb/ft3) Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi) Elongation at Break11 % Specific Heat Capacity840 J/kg-K Strength to Weight Ratio162 kN-m/kg Tensile Strength: Ultimate (UTS)450 MPa (65 x 103 psi) Tensile Strength: Yield (Proof)390...
    • 7021-milled
      Contact Now

      7021-milled

      Density2.78 g/cm3 (174 lb/ft3) Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi) Elongation at Break11 % Specific Heat Capacity840 J/kg-K Strength to Weight Ratio162 kN-m/kg Tensile Strength: Ultimate (UTS)450 MPa (65 x 103 psi) Tensile Strength: Yield (Proof)390...
    • 5083-Sawn
      Contact Now

      5083-Sawn

      Density2.66 g/cm3 (166 lb/ft3) Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi) Electrical Conductivity29 % IACS Elongation at Break17 % Fatigue Strength (Endurance Limit)150 MPa (22 x 103 psi) Melting Onset (Solidus)574 °C (1070 °F) Shear Modulus27 GPa (3.9 106...
    • 5083-milled
      Contact Now

      5083-milled

      Density2.66 g/cm3 (166 lb/ft3) Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi) Electrical Conductivity29 % IACS Elongation at Break17 % Fatigue Strength (Endurance Limit)150 MPa (22 x 103 psi) Melting Onset (Solidus)574 °C (1070 °F) Shear Modulus27 GPa (3.9 106...
Asian Aluminium Depot Co.,Ltd is one of the top level China moulding and tools manufacturers and suppliers with one the most famous bulk brands, if you are going to wholesale customized bulk moulding and tools in stock or you are looking for precision machined cast aluminium plates, cast plate, sawn aluminium plates, g.al dynamic, cast aluminium block, precision machined cast plate, high precision cast aluminium product free sample, we are always at your services.

Our Service

The company have a good and long-term strategic cooperative relationship with Chinalco, Nanshan Aluminum, WANJI Aluminium, ZhongFu Industrial, and so on which are domestic well-known brand aluminium manufacturers.

Feedback

Contact Us

Address:No.78 Gucheng Road(M.) Yushan Town, Kunshan City, Jiangsu Provice, China

Tel: +0086-512-36630592

Fax: +0086-512-36630595

E-mail: info@al-plate.com

CopyRight© Asian Aluminium Depot Co.,Ltd