Classification By Field Of Application

    • 1100
      Contact Now

      1100

      Density2.71 g/cm3 (169 lb/ft3) Elastic (Young's, Tensile) Modulus69 GPa (10 x 106 psi) Electrical Conductivity58 % IACS Elongation at Break5 % Melting Onset (Solidus)643 °C (1190 °F) Shear Modulus26 GPa (3.8 106 psi) Specific Heat Capacity900 J/kg-K Strength to Weight...
    • 1060
      Contact Now

      1060

      Density2.71 g/cm3 (169 lb/ft3) Elastic (Young's, Tensile) Modulus69 GPa (10.0 x 106 psi) Electrical Conductivity62 % IACS Elongation at Break6 % Fatigue Strength (Endurance Limit)45 MPa (6.5 x 103 psi) Melting Onset (Solidus)646 °C (1190 °F) Shear Strength75 MPa (11 x 103...
    • 1050
      Contact Now

      1050

      Base Metal Price16 % rel Density2.71 g/cm3 (169 lb/ft3) Elastic (Young's, Tensile) Modulus69 GPa (10.0 x 106 psi) Electrical Conductivity61 % IACS Elongation at Break6 % Melting Onset (Solidus)646 °C (1190 °F) Specific Heat Capacity900 J/kg-K Strength to Weight Ratio52...
    • 4343
    • 3003+Zn
    • 3003
      Contact Now

      3003

      Density2.73 g/cm3 (170 lb/ft3) Elastic (Young's, Tensile) Modulus69 GPa (10 x 106 psi) Electrical Conductivity42 % IACS Elongation at Break28 % Melting Onset (Solidus)643 °C (1190 °F) Shear Modulus26 GPa (3.8 106 psi) Specific Heat Capacity890 J/kg-K Strength to Weight...
    • 6008-T5
      Contact Now

      6008-T5

      Density2.70g/cm3 Density2.71 g/cm3 (169 lb/ft3) Elastic (Young's, Tensile) Modulus70 GPa (10 x 106 psi) Elongation at Break10 to 17 % Specific Heat Capacity890 J/kg-K Strength to Weight Ratio74 to 111 kN-m/kg Tensile Strength: Ultimate (UTS)200 to 300 MPa (29 to 44 x 103...
    • 6005-AT5
      Contact Now

      6005-AT5

      Density2.72g/cm3 Density2.71 g/cm3 (169 lb/ft3) Elastic (Young's, Tensile) Modulus70 GPa (10 x 106 psi) Electrical Conductivity50 % IACS Elongation at Break11 % Melting Onset (Solidus)605 °C (1120 °F) Shear Modulus26 GPa (3.8 106 psi) Specific Heat Capacity890 J/kg-K...
    • 7075-T651
      Contact Now

      7075-T651

      Density2.80 g/cm3 (175 lb/ft3) Elastic (Young's, Tensile) Modulus72 GPa (10 x 106 psi) Electrical Conductivity33 % IACS Elongation at Break10 % Melting Onset (Solidus)477 °C (890 °F) Shear Modulus27 GPa (3.9 106 psi) Specific Heat Capacity960 J/kg-K Strength to Weight...
    • 5083-H321
      Contact Now

      5083-H321

      Density2.66 g/cm3 (166 lb/ft3) Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi) Electrical Conductivity29 % IACS Elongation at Break15 % Melting Onset (Solidus)574 °C (1070 °F) Shear Modulus27 GPa (3.9 106 psi) Specific Heat Capacity900 J/kg-K Strength to Weight...
    • 7050-T7452
      Contact Now

      7050-T7452

      Density2.80 g/cm3 (175 lb/ft3) Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi) Elongation at Break8 to 9 % Specific Heat Capacity800 J/kg-K Strength to Weight Ratio193 to 196 kN-m/kg Tensile Strength: Ultimate (UTS)540 to 550 MPa (78 to 80 x 103 psi) Tensile...
    • 7N01
Asian Aluminium Depot Co.,Ltd is one of the top level China classification by field of application manufacturers and suppliers with one the most famous bulk brands, if you are going to wholesale customized bulk classification by field of application in stock or you are looking for classification by field of application free sample, we are always at your services.

Our Service

The company have a good and long-term strategic cooperative relationship with Chinalco, Nanshan Aluminum, WANJI Aluminium, ZhongFu Industrial, and so on which are domestic well-known brand aluminium manufacturers.

Feedback

Contact Us

Address: No.78 Gucheng Road(M.) Yushan Town, Kunshan City, Jiangsu Provice, China

Tel: +0086-512-36630592

Fax: +0086-512-36630595

E-mail: info@al-plate.com

CopyRight© Asian Aluminium Depot Co.,Ltd