Aerospace

    • 7055-T7751
      Contact Now

      7055-T7751

      Description Al alloy 7055 in the -T7751 temper for plate and the -T77511 for extrusions in 1991. This new 7XXX alloy was specifically developed for use in compression-dominated structures and provides advantages over alloy 7150 in compressive and tensile strengths while...
    • 7050-T7452
      Contact Now

      7050-T7452

      Density2.80 g/cm3 (175 lb/ft3) Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi) Elongation at Break8 % Specific Heat Capacity800 J/kg-K Strength to Weight Ratio193 kN-m/kg Tensile Strength: Ultimate (UTS)540 MPa (78 x 103 psi) Tensile Strength: Yield (Proof)460 MPa...
    • 7050-T7651
    • 7050-T7451
      Contact Now

      7050-T7451

      Alloy 7050 aluminum plates are the principal choice for aerospace applications, especially in the 3-6 inch thickness range. It exhibits better toughness/corrosion resistance characteristics than the older, more established alloy 7075. Since it is less quench sensitive than...
    • 7075-T7651
      Contact Now

      7075-T7651

      Density2.80 g/cm3 (175 lb/ft3) Elastic (Young's, Tensile) Modulus72 GPa (10 x 106 psi) Electrical Conductivity33 % IACS Elongation at Break10 % Melting Onset (Solidus)477 °C (890 °F) Shear Modulus27 GPa (3.9 106 psi) Specific Heat Capacity960 J/kg-K Strength to Weight...
    • 7075-T7351
      Contact Now

      7075-T7351

      Density2.80 g/cm3 (175 lb/ft3) Elastic (Young's, Tensile) Modulus72 GPa (10 x 106 psi) Electrical Conductivity33 % IACS Elongation at Break12 % Melting Onset (Solidus)477 °C (890 °F) Shear Modulus27 GPa (3.9 106 psi) Specific Heat Capacity960 J/kg-K Strength to Weight...
    • 7075-T651
      Contact Now

      7075-T651

      T651 temper 7075 has an ultimate tensile strength of 83000 psi (572 MPa) and yield strength of 73000 psi (503 MPa). It has a failure elongation of 3–9%. These properties can change depending on the form of material used. Thicker plate may exhibit lower strengths and...
    • 5A06-H112
    • 5A06-O
    • 2219-T851
      Contact Now

      2219-T851

      Density2.85 g/cm3 (178 lb/ft3) Elastic (Young's, Tensile) Modulus74 GPa (11 x 106 psi) Electrical Conductivity30 % IACS Elongation at Break10 % Fatigue Strength (Endurance Limit)103 MPa (15 x 103 psi) Melting Onset (Solidus)543 °C (1010 °F) Specific Heat Capacity860...
    • 2219-T651
      Contact Now

      2219-T651

      Density 2.84g/cm3
    • 2A14-T851
First Prev 12 Next Last 1/2
Asian Aluminium Depot Co.,Ltd is one of the top level China aerospace manufacturers and suppliers with one the most famous bulk brands, if you are going to wholesale customized bulk aerospace in stock or you are looking for 2000 series, 5000 series, 6000 series, 7000 series, aluminum high quality applications, aerospace aluminum, aircraft alloy, pre-stretching plate, aircraft frames, hardest alloys free sample, we are always at your services.

Our Service

The company have a good and long-term strategic cooperative relationship with Chinalco, Nanshan Aluminum, WANJI Aluminium, ZhongFu Industrial, and so on which are domestic well-known brand aluminium manufacturers.

Feedback

Contact Us

Address:No.78 Gucheng Road(M.) Yushan Town, Kunshan City, Jiangsu Provice, China

Tel: +0086-512-36630592

Fax: +0086-512-36630595

E-mail: info@al-plate.com

CopyRight© Asian Aluminium Depot Co.,Ltd