5252-H111

5252-H111

Density2.68 g/cm3 (167 lb/ft3) Elastic (Young's, Tensile) Modulus70 GPa (10 x 106 psi) Electrical Conductivity35 % IACS Elongation at Break22 % Melting Onset (Solidus)607 °C (1120 °F) Shear Modulus26 GPa (3.8 106 psi) Specific Heat Capacity900 J/kg-K Strength to Weight Ratio71 kN-m/kg...

Product details

Density2.68 g/cm3 (167 lb/ft3)

Elastic (Young's, Tensile) Modulus70 GPa (10 x 106 psi)

Electrical Conductivity35 % IACS

Elongation at Break22 %

Melting Onset (Solidus)607 °C (1120 °F)

Shear Modulus26 GPa (3.8 106 psi)

Specific Heat Capacity900 J/kg-K

Strength to Weight Ratio71 kN-m/kg

Tensile Strength: Ultimate (UTS)190 MPa (28 x 103 psi)

Tensile Strength: Yield (Proof)80 MPa (12 x 103 psi)

Thermal Conductivity140 W/m-K

Thermal Diffusivity58

Thermal Expansion23.8 µm/m-K

Hot Tags: 5252H111 Electronics
Related Products
Feedback

Our Service

The company have a good and long-term strategic cooperative relationship with Chinalco, Nanshan Aluminum, WANJI Aluminium, ZhongFu Industrial, and so on which are domestic well-known brand aluminium manufacturers.

Feedback

Contact Us

Address:No.78 Gucheng Road(M.) Yushan Town, Kunshan City, Jiangsu Provice, China

Tel: +0086-512-36630592

Fax: +0086-512-36630595

E-mail: info@al-plate.com

CopyRight© Asian Aluminium Depot Co.,Ltd