Density2.70 g/cm3 (169 lb/ft3) Elastic (Young's, Tensile) Modulus70 GPa (10 x 106 psi) Electrical Conductivity52 % IACS Elongation at Break26 % Melting Onset (Solidus)630 °C (1170 °F) Shear Modulus26 GPa (3.8 106 psi) Specific Heat Capacity900 J/kg-K Strength to Weight Ratio48 kN-m/kg...

Product details

Density2.70 g/cm3 (169 lb/ft3)

Elastic (Young's, Tensile) Modulus70 GPa (10 x 106 psi)

Electrical Conductivity52 % IACS

Elongation at Break26 %

Melting Onset (Solidus)630 °C (1170 °F)

Shear Modulus26 GPa (3.8 106 psi)

Specific Heat Capacity900 J/kg-K

Strength to Weight Ratio48 kN-m/kg

Tensile Strength: Ultimate (UTS)130 MPa (19 x 103 psi)

Tensile Strength: Yield (Proof)50 MPa (7.3 x 103 psi)

Thermal Conductivity200 W/m-K

Thermal Diffusivity82

Thermal Expansion23.5 µm/m-K

Hot Tags: 5005H111 Cooking Utensils
Related Products
Feedback

Our Service

The company have a good and long-term strategic cooperative relationship with Chinalco, Nanshan Aluminum, WANJI Aluminium, ZhongFu Industrial, and so on which are domestic well-known brand aluminium manufacturers.

Feedback

Contact Us

Address:No.78 Gucheng Road(M.) Yushan Town, Kunshan City, Jiangsu Provice, China

Tel: +0086-512-36630592

Fax: +0086-512-36630595

E-mail: info@al-plate.com

CopyRight© Asian Aluminium Depot Co.,Ltd